Batteries with silicon anodes: Neutron experiments show how formation of surface structures reduces amp-hour capacity

Neutrons (red arrows) detect the presence of Lithium ions which have migrated into the silicon anode.

Neutrons (red arrows) detect the presence of Lithium ions which have migrated into the silicon anode. © HZB

In theory, silicon anodes could store ten times more lithium ions than graphite anodes, which have been used in commercial lithium batteries for many years. However, the amp-hour capacity of silicon anodes so far has been declining sharply with each additional charge-discharge cycle. Now an HZB team at BER II of the HZB in Berlin and the Institut Laue-Langevin in Grenoble has utilised neutron experiments to establish what happens at the surface of the silicon anode during charging and what processes reduce this capacity.

”With the neutron experiments and other measurements, we were able to observe how an inhibition or “blocking” layer forms on the silicon surface during charging that hinders the penetration of lithium ions”, explains HZB physicist Dr. Sebastian Risse. This 30-60 nanometre layer consists of organic molecules from the electrolyte liquid and inorganic components. When charging, the layer partially dissolves again so that the lithium ions can penetrate the silicon anode. However, energy is needed to dissolve the layer, which is then no longer available for storing. The physicists used the same electrolyte fluid in the experiment that is used in commercial lithium batteries.

Several cycles observed

After preliminary investigations with HZB’s BER II neutron source, the experiments at the Institut Laue-Langevin (ILL) in Grenoble provided a precise insight into the processes. ”Cold neutrons at very high flux are available at the ILL reactor. We were able to use them to non-destructively observe the silicon anode during several charge cycles”, explains Risse. Using a measuring cell developed at the HZB, physicists were able to examine the silicon anodes with neutrons during the charge-discharge cycles (in operando) and also record a number of other measurement values such as electrical resistance using impedance spectroscopy.

Efficiencies of 94 %

As soon as this inhibition layer is dissolved, the efficiency of the charge-discharge cycles increases to 94 per cent (94 % of the stored charge can be delivered again). This value is higher than that of lead-acid batteries (90 %), but slightly lower than that of batteries employing more highly developed lithium-ion technology, which deliver up to 99.9 %.

Outlook: Preventing the blocking layer

”We now want to investigate whether it is possible to prevent the formation of this inhibition or “blocking” layer by applying a very thin protective layer of metal oxide so that the capacity of silicon anodes decreases less over the course of many charge-discharge cycles”, says Risse.

The study was published in „Energy Storage Materials“: "Surface structure inhibited lithiation of crystalline silicon probed with operando neutron reflectivity". Arne Ronneburg, Marcus Trapp, Robert Cubitt, Luca Silvi,  Sébastien Cap, Matthias  Ballauff, Sebastian Risse.

DOI: 10.1016/j.ensm.2018.11.032

arö

  • Copy link

You might also be interested in

  • New instrument at BESSY II: The OÆSE endstation in EMIL
    Science Highlight
    23.04.2025
    New instrument at BESSY II: The OÆSE endstation in EMIL
    A new instrument is now available at BESSY II for investigating catalyst materials, battery electrodes and other energy devices under operating conditions: the Operando Absorption and Emission Spectroscopy on EMIL (OÆSE) endstation in the Energy Materials In-situ Laboratory Berlin (EMIL). A team led by Raul Garcia-Diez and Marcus Bär showcases the instrument’s capabilities via a proof-of-concept study on electrodeposited copper.
  • Green hydrogen: A cage structured material transforms into a performant catalyst
    Science Highlight
    17.04.2025
    Green hydrogen: A cage structured material transforms into a performant catalyst
    Clathrates are characterised by a complex cage structure that provides space for guest ions too. Now, for the first time, a team has investigated the suitability of clathrates as catalysts for electrolytic hydrogen production with impressive results: the clathrate sample was even more efficient and robust than currently used nickel-based catalysts. They also found a reason for this enhanced performance. Measurements at BESSY II showed that the clathrates undergo structural changes during the catalytic reaction: the three-dimensional cage structure decays into ultra-thin nanosheets that allow maximum contact with active catalytic centres. The study has been published in the journal ‘Angewandte Chemie’.
  • An elegant method for the detection of single spins using photovoltage
    Science Highlight
    14.04.2025
    An elegant method for the detection of single spins using photovoltage
    Diamonds with certain optically active defects can be used as highly sensitive sensors or qubits for quantum computers, where the quantum information is stored in the electron spin state of these colour centres. However, the spin states have to be read out optically, which is often experimentally complex. Now, a team at HZB has developed an elegant method using a photo voltage to detect the individual and local spin states of these defects. This could lead to a much more compact design of quantum sensors.