Spintronics: Resetting the future of Heat Assisted Magnetic Recording

The nanostructured membrane has a honeycomb pattern with nanoholes of 68 nm in diameter. The nanoholes pin down the magnetic domains.

The nanostructured membrane has a honeycomb pattern with nanoholes of 68 nm in diameter. The nanoholes pin down the magnetic domains. © HZB

A thin film of Dysprosium-Cobalt (green) has been sputtered on top of the membrane, resulting in an array of antidots. The magnetic moments of DyCo<sub>5</sub> are perpendicular to the plane and stable against external magnetic fields. A laser pulse can be used to locally increase the temperature of individual bits.

A thin film of Dysprosium-Cobalt (green) has been sputtered on top of the membrane, resulting in an array of antidots. The magnetic moments of DyCo5 are perpendicular to the plane and stable against external magnetic fields. A laser pulse can be used to locally increase the temperature of individual bits. © HZB

Moderate heating up to 80 &deg;Celsius does tilt the magnetic moment associated to a single bit into the plane. Upon cooling to room temperature, the magnetic moment stays in plane, until it is overwritten by a magnetic writing head.

Moderate heating up to 80 °Celsius does tilt the magnetic moment associated to a single bit into the plane. Upon cooling to room temperature, the magnetic moment stays in plane, until it is overwritten by a magnetic writing head. © HZB

A HZB team has examined thin films of Dysprosium-Cobalt sputtered onto a nanostructured membrane at BESSY II. They showed that new patterns of magnetization could be written in a quick and easy manner after warming the sample to only 80 °Celsius, which is a much lower temperature as compared to conventional Heat Assisted Magnetic Recording systems. This paves the way to fast and energy efficient ultrahigh density data storage. The results are published now in the new journal Physical Review Applied.

To increase data density further in storage media, materials systems with stable magnetic domains on the nanoscale are needed. For overwriting a specific nanoscopic region with new information, a laser is used to heat locally the bit close to the so called Curie-Temperature, typically several hundred degrees Celsius. Upon cooling, the magnetic domain in this region can be reoriented in a small external magnetic field, known as Heat Assisted Magnetic Recording (HAMR). In industry, Iron-Platinum materials are currently used as magnetic media for the development of such HAMR-data storage devices.

Magnetic signals mapped at BESSY II before and after heating

A HZB team has now examined a new storage media system of Dysprosium and Cobalt, which shows key advantages with respect to conventional HAMR materials: A much lower writing temperature, a higher stability of the magnetic bits, and a versatile control of the spin orientation within individual magnetic bits. They achieved this by sputtering a thin film of Dysprosium and Cobalt onto a nanostructured membrane. The membrane was produced by scientific cooperation partners at the Institute of Materials Science of Madrid. The system shows a honeycomb antidot pattern with distances of 105 nanometers between nanoholes, which are 68 nanometers in diameter. These nanoholes act themselves as pinning centers for stabilizing magnetic wall displacements. The magnetic moments of DyCo5 are perpendicular to the plane and stable against external magnetic fields.

Energy efficient process

HZB-physicist Dr. Jaime Sánchez-Barriga and his team could demonstrate that warming the system to only 80 degrees Celsius is sufficient to tilt the magnetic moments in the DyCo5 film parallel to the surface plane. With measurements at the PEEM and XMCD instruments at BESSY II they could map precisely the magnetic signals before, during and after warming. After cooling to room temperature it is then easy to reorient the magnetic domains with a writing head and to encode new information. “This process in DyCo5 is energy efficient and very fast”, states Dr. Florin Radu, co-author of the study. “Our results show that there are alternative candidates for ultrahigh density HAMR storage systems, which need less energy and promise other important advantages as well”, adds Sánchez-Barriga.

Publication: Ferrimagnetic DyCo5 nanostructures for bits in heat-assisted magnetic recording.  A. A. Ünal, S. Valencia, F.  Radu, D. Marchenko, K. J. Merazzo, M. Vázquez, and J. Sánchez-Barriga, Phys. Rev. Applied 5, 064007
Doi: http://dx.doi.org/10.1103/PhysRevApplied.5.064007

arö


You might also be interested in

  • Fertilisation under the X-ray beam
    Science Highlight
    19.03.2024
    Fertilisation under the X-ray beam
    After the egg has been fertilized by a sperm, the surrounding egg coat tightens, mechanically preventing the entry of additional sperm and the ensuing death of the embryo. A team from the Karolinska Institutet has now gained this new insight through measurements at the X-ray light sources BESSY II, DLS and ESRF. 
  • Neutron experiment at BER II reveals new spin phase in quantum materials
    Science Highlight
    18.03.2024
    Neutron experiment at BER II reveals new spin phase in quantum materials
    New states of order can arise in quantum magnetic materials under magnetic fields. An international team has now gained new insights into these special states of matter through experiments at the Berlin neutron source BER II and its High-Field Magnet. BER II served science until the end of 2019 and has since been shut down. Results from data at BER II are still being published.

  • Where quantum computers can score
    Science Highlight
    15.03.2024
    Where quantum computers can score
    The travelling salesman problem is considered a prime example of a combinatorial optimisation problem. Now a Berlin team led by theoretical physicist Prof. Dr. Jens Eisert of Freie Universität Berlin and HZB has shown that a certain class of such problems can actually be solved better and much faster with quantum computers than with conventional methods.