• Arlt, T.; Klages, M.; Messerschmidt, M.; Scholta, J.; Manke, I.: Influence of artificially aged gas diffusion layers on the water management of polymer electrolyte membrane fuel cells analyzed with in-operando synchrotron imaging. Energy 118 (2017), p. 502-511

10.1016/j.energy.2016.10.061

Abstract:
The influence of artificial ageing of gas diffusion layers (GDLs) on the cell performance was investigated using high resolution synchrotron radiography. State-of-the-art GDLs of the type SIGRACET® SGL 25BC were aged for 0 h, 16 h and 24 h in a hydrogen peroxide solution before they were assembled in the fuel cells. In-operando radiographic measurements were combined with voltage and contact angle measurements. Correlations between applied ageing conditions, GDL water saturation and cell performance were revealed. Hereby, all cell operating conditions were tested several times to estimate the reproducibility of in-operando radiographic fuel cell measurements. Water films at the GDL-membrane and at the GDL-flow field interfaces were found and attributed to MPL cracks and large pores in the GDL structure. The combination of these cracks and pores are assumed to play a crucial role for blocked gas paths, leading to an undersupply with reactants and an increased humidification of the membrane. It is shown that water agglomerations directly impact the membrane resistance. We assume that the hydrophobicity of the fibers inside the GDL is more important for the cell performance than water agglomerations at the membrane-GDL interface.