Chang, C.S.T.; De Geuser, F.; Banhart, J.: In situ characterization of β precipitation in an Al–Mg–Si alloy by anisotropic small-angle neutron scattering on a single crystal. Journal of Applied Crystallography 48 (2015), p. 455-463
10.1107/S1600576715002770
Open Access Version (externer Anbieter)
Abstract:
A single crystal of an Al–Mg–Si alloy (Mg: 0.43 wt%, Si: 0.47 wt%) was aged at 453 K while small-angle neutron scattering experiments were carried out in situ. The scattering data recorded on a two-dimensional detector show the symmetry typical for needle-shaped 00 precipitates oriented in the three [100] directions of the aluminium lattice and allow the calculation of the length, diameter and number density of the precipitates assuming cylindrical scattering objects of equal size and composition. The repetition time of the experiments was 12 min. The values obtained for the three quantities agree well with values measured by transmission electron microscopy (TEM) on a similar alloy. The impact of one week of natural ageing before artificial ageing on the evolution of the size and number density of precipitates is found to be pronounced, as expected from published TEM data.